粉末冶金/硬質合金/金剛石工具粉末系列(Powders for Powder metallurgy/Cemented carbide/diamond tools)名稱牌號典型成分(wt%)粒度(mesh)松比(g/cm3)氧含量(%)還原鎳粉FNi-還Ni≥99.5Fsss≤4.0μm1.3≤0.2霧化鎳粉FNi-霧Ni≥99.8-3002.8≤0.2還原鈷粉FCo-還Co≥99.7Fsss: 0.6-2.0μm1.0≤0.3錫粉FSnSn≥99.9-2003.4≤0.2鋅粉FZnZn≥99.7-2003.2≤0.3硅粉FSiSi≥99.0-2000.3≤0.6鉬粉FMoMo≥99.9Fsss: 2.0-4.0μm1.1≤0.2鉻粉FCrCr≥99.0-2502.8≤0.5鈦粉FTiTi≥99.0-2501.4≤0.5鋁硅粉FAlSi10Si:10.0 Al余-2001.3≤0.3碳化鈦粉FTiCTiC≥99.5 C:19.5Fsss: 2.0-4.0μm1.2≤0.5錳粉FMnMn≥99.0-2002.6≤0.5鈷碳化鎢FYG8Co8.0 WC余-3002.9≤0.3磷鐵粉FFeP25P≥25.0 Fe余-2002.4≤0.4錳鐵粉F78MnFeMn78.0 C8.0 Fe余-2002.5≤0.4F75MnFeMn75.0 C2.0 Fe余-200磷銅粉FCuP14P14.0 Cu余-2002.1≤0.5FCuP8P8.0 Cu余-200    銅合金FCuSn10Sn10.0 Cu余-200, -3003.5≤0.1FCuSn15Sn15.0 Cu余-200,-3003.4≤0.1FCuSn20Sn20.0 Cu余-200,-3002.9≤0.1FCuSn40Sn40.0 Cu余-200,-3003.2≤0.1F660Sn6.0 Zn6.0 Cu余-200,-3003.6≤0.1FCuRe5Re5 Cu 余-200,-3002.9≤0.2FCuZn20Zn20.0 Cu余-200,-3003.3≤02FCuZn30Zn30.0 Cu余-200,-3003.5≤0.2  不銹鋼粉430LCr17.0 Fe余-100,-400>4.2≤0.1304LCr19.0 Ni:10.0 Fe余-100,-400>4.2≤0.1316LCr17.0 Ni12.0 Mo2.5 Fe余-100,-400>4.2≤0.1310SCr25 Ni20.5 Fe余-100,-400>4.2≤0.117-4 PHCr16.5Ni4.5Cu4.0Nb0.3Fe余-100,-400>4.2≤0.1電解鎳粉FNi-電Ni+Co≥99.5-3001.0≤0.3羰基鎳粉FNi-羰Ni≥99.8Fsss: 2.0-3.0μm0.6≤0.2羰基鐵粉FFe-羰Fe≥98.5Fsss:1.5-3.0μm1.0≤0.4還原鐵粉FFeFe≥98.5-2002.6≤0.3電解銅粉FCu-電Cu≥99.6-3001.7≤0.3氫化鈦粉FTiHTiH≥99.5-2501.3≤0.5鎢粉FWW≥99.85Fsss≤4.0μm3.5≤0.25碳化鎢粉FWCWC≥99.7 C:6.13±0.05Fsss≤4.0μm4.3≤0.2鑄造碳化鎢粉FZWCW:95.0-96.0 C:3.9±0.1 60/80   80/120 120/200 200/4006.7≤0.2

注射成型粉末系列(Powders for MIM)牌  號Designation典 型 成 分 /wt%Typical Component430LCr17.0 Si1Mn1 Fe余434Cr17 Si1 C0.12 Fe余304LCr19Ni10 Si1 Mn2 Fe余316LCr17 Ni12 Si1Mo2.5Mn2 Fe余310SCr25 Ni20.5 Si1.5 Mn2Fe余15-5 PHCr15 Si1Mn1 Cu3.5Nb0.3 Fe余17-4 PHCr16.5 Ni4.5 Si1 Mn1 Cu4 Nb0.3 Fe余17-7 PHCr17 Si1 Mn1 Al1.3 Fe余A6Cr1 Ni0.3 Si0.5Mo1.2Mn2.2 C0.7 Fe 余D2Cr 12 Ni0.3 Si0.6 Mo1 Mn0.6 V1.1 C 1.5Fe 余H13Cr5.12 Ni0.3 Si1 Mo1.43 Mn0.35V1 C0.39 Fe 余M2Cr4.13 Ni0.3 Si0.3 Mo5 Mn0.28 W6.13 V1.98 C0.92Fe 余S2Ni0.3 Si1 Mo0.45 Mn0.4 V0.5 C0.48 Fe 余T15Cr4.38Ni0.3 Si0.3 Mo1 Mn0.28W12.38V4.88Co5 C1.55Fe 余 注射成形用粉末粒度分布(μm)Typical particle size distribution for MIM powder (μm)D10 (%)D50 (%)D90 (%)– 38 μm5.513.031.0– 32μm5.012.029.080% – 22μm4.511.527.090% – 22μm4.010.522.090% – 16μm3.58.016.0

釬焊合金粉末系列(Brazingalloy powders)名稱Name國標牌號Standard Designation我所原用牌號 DesignationAWS牌號AWS Designation典 型 成 分 / %wtTypical Component粒度/ mesh Particle Size釬焊溫度/oCBrazing Temp.鎳基釬焊粉BNi82CrSiBFeQFNi-01BNi-2Cr7B3Si4.5Fe3Ni余-200,-3001010-1175BNi92SiBQFNi-02BNi-3B3Si4.5Ni余-200,-3001010-1175BNi95SiBQFNi-03BNi-4B1.8Si3.5Ni余-200,-3001010-1175BNi73CrFeSiB(C)QFNi-04BNi-1Cr14B3.1Si4.5Fe4.5C:0.7Ni余-200,-3001065-1205BNi74CrFeSiBQFNi-05BNi-1ACr14B3.1Si4.5Fe4.5Ni余-200,-3001075-1205BNi71CrSiQFNi-06BNi-5Cr19Si10Ni余-200,-3001150-1205BNi89PBNi89PBNi-6P11Ni余-200,-300925-1025BNi76CrPBNi76CrPBNi-7Cr14P10Ni余-200,-300925-1040BNi66MnSiCuBNi66MnSiCuBNi-8Cu4.5Si7Mn23Ni余-200,-3001010-1095BNi81CrBBNi81CrBBNi-9Cr15B3.5Ni余-200,-3001066-1204BNi63WCrFeSiBBNi63WCrFeSiBBNi-10C0.45B2.5Cr11.5Si3.5Fe3.5W16Ni余-200,-3001150-1205BNi67WCrSiFeBQFNi-07BNi-11C0.4B2.5Cr10Si3.5Fe3W12Ni余-200,-3001150-1205BNi65CrPBNi65CrPBNi-12Cr25P10Ni余-200,-300980-1095BNi78CrSiBCuMoNbBNi78CrSiBCuMoNbBNi-13B3Cr8Si4.3Cu2.5Mo2Nb2Ni余-200,-3001095-1175QFNi58CrCoAlTaBCr24Co9Al3Ta2.5B3Ni余-200,-3001150-1250鈷基釬焊粉QFCo-01BCo-1Cr19Ni17W4Si8B0.8C0.4Co余-200,-3001150-1232QFCo-02Cr19Ni18W10Si3B3.5C0.8Co余-200,-3001150-1250銅基釬焊粉BCuBCuBCu-1Cu≥99.90-200,-3001080-1180BCuSnBCuSnSn10Cu余-200,-300840-1000BCu54ZnBCu54ZnCu54Zn余-200,-300890-950BCu57ZnMnCoBCu57ZnMnCoCu57Mn2Co2Zn余-200,-300930-990BCu58ZnMnBCu58ZnMnCu58Mn4Zn余-200,-300910-980BCu60ZnSnBCu60ZnSnCu60Sn1Si0.2Zn余-200,-300910-970BCu80AgPBCu80AgPAg15P5Cu余-200,-300700-800BCu86SnPBCu86SnPSn7P6.8Cu余-200,-300700-780BCu89PAgBCu89PAgAg5P6.3Cu余-200,-300710-800BCu93PBCu93PBCuP-2P7Cu余-200,-300732-843BCu69NiSiBNi28.5Si1.7B0.2Cu余-200,-300935-1050BCuZnNiRBCuZn-DZn42Ni10Cu余-200,-300938-982BCuMnNiMn10Ni3Cu余-200,-300930-985BCuMnCoMn10Co3Cu余-200,-300940-990鋁基釬焊粉BAl86SiCuQFAl-01BAlSi-3Si10Cu4Al余-200,-300571-604BAl88SiQFAl-02BAlSi-4Si12Al余-200,-300582-604BAl90SiQFAl-03BAlSi-5Si10Al余-200,-300588-604BAl89SiMgQFAl-04BAlSi-7Si10Mg1.5Al余-200,-300588-604BAl92SiQFAl-05BAlSi-2Si7.5Al余-200,-300599-621銀基釬焊粉BAg40CuZnNiBAg-4Ni2Zn28Cu30Ag余-200,-300779-899BAg45CuZnBAg-5Zn25Cu30Ag余-200,-300743-843BAg56CuZnSnBAg-7Sn5Zn17Cu22Ag余-200,-300652-760BAg72CuBAg-8Cu28Ag余-200,-300779-899BAg56CuNiBAg-13aNi2Cu42Ag余-200,-300871-982BAg60CuSnBAg-18Sn10Cu30Ag余-200,-300718-843BAg49CuZnMnNiBAg-22Mn7.5Ni4.5Zn23Cu16Ag余-200,-300699-830BAg85MnBAg-23Mn15Ag余-200,-300970-1038BAg49CuZnNiBAg-24Ni2Zn28Cu20Ag余-200,-300707-843

金剛石預合金粉末系列(Pre-alloy powders for diamond tools)牌號典型成分(wt%)粒度(mesh)參考燒結溫度(℃)松比(g/cm3)理論密度(g/cm3)備注FJT-A1Co14Cu13Sn4Fe余-300,-400780-8602.98.12基礎合金粉,推薦用于硬花崗巖的高檔小徑鋸片。FJT-A2 Cu30Fe余-300,-400800-8802.98.17水霧化Fe-Cu合金粉末,低氧,超細,用于各種金剛石制品作為基礎合金粉使用。FJT-A3Ni13Fe37Sn9Cu余-300,-400760-8603.28.38基礎合金粉末,用于中高檔石材鋸片。 FJT-A4 Co27Fe23Cu余-300,-400           780-8603.08.67含鈷基礎粉,耐磨性高,對金剛石把持力強,可用于高檔石材鋸片、工程薄壁鉆、水泥鋸片等。FJT-A5Ni10Co27Fe14Sn9Cu余-300,-400780-8602.98.62基礎合金粉,用于各種鋒利性金剛石制品。FJT-A6Co42Cu23Fe余-300,-400800-8602.88.54高鈷基礎合金粉,推薦用于薄壁鉆頭、高檔金剛石工具等。FJT-A9 Cu40Fe余-300,-400780-8602.9 8.28水霧化Fe-Cu合金粉末,低氧,超細,用于各種金剛石制品作為基礎合金粉使用。 FJT-A10 Cu41Sn5Fe余-300,-400760-8502.98.27氧含量低,合金化完全,有效提高了胎體抗彎強度,金剛石出露較高,適于加工陶瓷類工具。FJT-A11 Cu16Co20Fe余-300,-400800-8802.88.24含鈷基礎粉,耐磨性高,對金剛石的把持力強,可用于高檔石材鋸片、工程薄壁鉆、水泥鋸片等。FJT-01 Cr6B3Si4Fe2Ni余-300,-400840-8803.98.32低熔點鎳基合金粉,代替鎳粉使用,也作添加劑,熔點比鎳粉低約400℃,硬度比鎳粉高,可提高附著力。FJT-02 Si2B2Cu20Fe4Ni余 -300,-400840-8705.38.60低熔點鎳基合金粉,代替鎳粉使用,也作添加劑,熔點比鎳粉低約400℃,硬度比FJT-01低,可提高鋒利度。FJT-03Si4B2Cr18Fe2Ni29Co余-300,-400850-8905.0 8.18低熔點鈷基合金粉,用作高檔金剛石工具的添加劑,降低燒結溫度,提高附著力,減小WC用量。FJT-06 Cr5B3Si4Ni30Fe余-300,-400860-900 3.8 7.75低熔點鐵基合金粉,用作中、高檔金剛石工具的添加劑,提高附著力,增加鋒利度,并部分替代WC。FJT-07Ni4W9Mo3Fe余-300,-400870-9203.59.01用作高檔金剛石工具的添加劑,提高附著力,增加鋒利度。FJT-08Cr14B3Si4Cu4Fe12Ni余-300,-400850-9003.88.08低熔點鎳基合金粉,代替鎳粉加入,也作添加劑,熔點比鎳粉低約400℃,提高附著力,增加鋒利度,減小WC用量。FW1Cu24Ni15Sn5Fe余-300,-400800-8603.18.24基礎合金粉末,對金剛石把持力強,金剛石出露高 ,磨損性能與鈷基胎體相近,適用于較大直徑鋸片。FW2Cu42Ni6Sn15Fe余-300,-400760-8603.08.28

熱噴涂及打底粉末系列(Thermalspray powders)類別Class牌 號Designation國標牌號Standard Designation典 型 成 分 (wt%)Typical Component熔點(oC)Fusion temp硬度(HRC)Hardness備         注Remarks鎳基噴涂粉LNi-02FPTN-150BCr15Si0.8Al0.3Fe4Ni余熔點≤1400HB180涂層具有良好的韌性和耐磨、耐蝕性,可用硬質合金切削加工,主要用于工件恢復尺寸,適用于火焰噴涂、超音速噴涂、等離子噴涂。LNi-04FPTN-200BCr14C0.4Si1.5B0.8Fe6Ni余熔點≤1400HB200LNi-05FPTN-250BCr11C0.8Si2.5B1.8Fe5Ni余熔點≤1400HB300LNiCrSiCr19Si10Ni余熔點≤120040新型的適合于氧乙炔火焰噴涂的耐磨涂層。抗高溫氧化腐蝕性、耐磨粒磨損性好,用于恢復尺寸或表面強化提高使用壽命,也適用于超音速噴涂、等離子噴涂。LNiCrWCr10W12Si3B2Fe2Ni余熔點≤120040LNiNi:≥99.5≤700<20高純球形霧化鎳粉,涂層致密易切削,耐蝕性好,適用于等離子噴涂、火焰噴涂、超音速噴涂、爆炸噴涂。LNi80Cr20Cr20Ni余≤90020耐磨性耐蝕性好,抗高溫氧化腐蝕涂層或陶瓷涂層的過渡層。適用于等離子噴涂、超音速噴涂、爆炸噴涂。LNi50Cr50Cr48Ni余≤90025鐵基及不銹鋼噴涂粉LFe-02FPTFCr15-320Cr16Ni4Cu2C2B1Si1Fe余熔點≤1250HB320耐磨、耐蝕、韌性好,用于軸類、葉片、造紙烘缸、印刷滾筒、柴油機汽缸、旋風分離器等的恢復尺寸與強化。適用于氧乙炔火焰噴涂、等離子噴涂、超音速噴涂、爆炸噴涂。LFe-03FPTFCr15-250Cr16Ni9Cu2C0.5B2Si2Fe余熔點≤1250HB240LFe-04FPTFCr18-320Cr16Ni4Cu2C0.1B2Si1Fe余熔點≤1250HB350L304Cr18 Ni9Fe余≤600HB260涂層硬度適中韌性好,耐腐蝕,耐低溫顆粒沖蝕,厚涂層不易開裂,用于恢復工件尺寸并提高工件耐磨壽命。涂層可進行車加工,且磨光性好。適用于等離子噴涂、超音速噴涂、爆炸噴涂。L316Cr17Ni14Mo2Fe余≤600HB260L430Cr17Fe余≤600HB300耐熱超高溫合金粉FCoCrAlYTaCr22Al11Y1Ta1Si2Co余≤110040鈷基超高溫合金,高溫打底用。涂層致密,抗高溫氧化性能優良。采用超音速噴涂、爆炸噴涂、等離子噴涂工藝,用于冶金軋輥、退火爐輥等的防結瘤涂層、航空發動機葉片、導向葉片和燃氣輪機葉片的耐熱涂層及噴氣發動機燃燒室加力筒和火焰筒熱障涂層的粘結過渡層。FCoCrAlYCr22Al11Y1Si2Co余≤110040FNiCrAlYCr22Al11Y1Si2Ni余≤95020-30鎳基超高溫合金,僅次于FCoCrAlY的高溫打底粉,采用超音速噴涂、爆炸噴涂、等離子噴涂工藝,用于冶金軋輥、熱浸鍍浸沒輥、熱處理爐輥等耐熱涂層;航空發動機葉片、燃氣輪機葉片的耐熱涂層以及高溫爐風口、防熱罩表面熱障涂層的粘結過渡層。FNiCoCrAlYCr18Al12Y1Si2.1Co23Ni余≤95020-30打底粉及復合粉FAl/NiFF01.04Al20 Ni余≤80020鎳包鋁:放熱型包覆粉末,抗氧化、熔蝕、抗熱沖擊;用于噴涂打底,也作為工作層用于修復與強化,如發動機部件、汽車曲軸、機床導軌等。FMoMo≥ 99.5%≤35020放熱性噴涂粉末,與基體結合強度高,涂層耐磨性好、抗粘結性能好。用于等離子打底或噴涂汽車同步環、活塞環等。FNiCrAlAl5 NiCr余≤90020鎳鉻鋁:放熱型復合粉,耐燃氣腐蝕,抗微震磨損,是高溫金屬涂層和高溫陶瓷涂層的優良粘結材料,也作高溫抗氧化工作涂層。